- Wall Curing Adhesive
- Vato toy ny Paint
- Loko rindrina anatiny
- Loko miloko
- Loko Latex ho an'ny rindrina ivelany
- SBS Liquid Coil Polyurethane Waterproof Coating
- RG Waterproof coating
- Polyurethane coating amin'ny rano
- Adhesive taila seramika
- Adhesive tsy tantera-drano mangarahara
- Compound adhesive
- Waterborne Industrial Paint Emulsion
- Coating Additive
- Rust Converter
- Fanamafisana harafesina
- Mpanamboatra fasika
- Adhesive mora tohina
- Emulsion FOOT
- Textile Emulsion
- Emulsion tsy tantera-drano
- Architectural Emulsion
Toilet sy ny tafo Acrylic sy Styrene Waterproof Emulsion HX-400 ho an'ny Thermal Insulation Mortar sy ny singa roa simenitra coating tantera-drano
famaritana2
tombony
masontsivana
Valiny fitsapana 400JS-IIType | |||
Zavatra andrana | Vokatra fitsapana | ||
Votoaty mafy: ≥ 70% | 76,5% | ||
Herin'ny tensile (STD ≥ 1.2Mpa) | 2.3 | 2.42 | 2.39 |
Elongation amin'ny fiatoana(STD ≥ 200%) | 123 | 138 | 129 |
Fahaizana hafanana ambany (radius 10mm rod) | -10 ℃ Tsy misy triatra | ||
Impermeability (0.3Mpa, 30Min) | tsy len-drano |
400JS- Ⅱ Karazana raikipohy soso-kevitra | |
Anaran'ny fitaovana | Fangaro mifangaro |
400 | 400 kg |
Rano | 100 kg |
hiteraka | 4 kg |
Defoaming | 5 kg |
AMP-95 | 3 kg |
TT-935 | sahaza ny vola |
42.5 simenitra Portland tsotra | 500 kg |
400 metatra toradroa | 200 kg |
80-120 meshes quartz vovoka | 300 kg |
400JS-IIType valin'ny fitsapana | |||
Zavatra andrana | Vokatra fitsapana | ||
Votoaty mafy: ≥ 70% | 74,7% | ||
Herin'ny tensile (STD ≥ 1.2Mpa) | 2.82 | 2.76 | 2.54 |
Elongation amin'ny fiatoana(STD ≥ 200%) | 268 | 271 | 282 |
Fahaizana hafanana ambany (radius 10mm rod) | -10 ℃ Tsy misy triatra | ||
Impermeability (0.3Mpa, 30Min) | tsy len-drano |
400JS- Ⅰ Karazana raikipohy soso-kevitra | |
Anaran'ny fitaovana | Fangaro mifangaro |
400 | 450 kg |
Rano | 50 kg |
hiteraka | 2Pj |
Defoaming | 2Pj |
AMP-95 | 1,5 kg |
TT-935 | Vola mety |
42.5 simenitra Portland tsotra | 250 kg |
400 metatra toradroa | 100 kg |
80-120 meshes quartz vovoka | 150 kg |
vokatra | Tg℃ | Votoaty mafy % | Viscosité (cps/25 ℃) | PH | MFFT ℃ |
HX-400 | -10 | 55±1 | 1000-1800 | 7-8 | 0 |